Peso specifico Kg/dm3:7.8
LAMIERE
ASTM / ASME:A/SA 240
EN:10028-7
TUBI SALDATI
ASTM / ASME:A/SA 790 – A 928
EN:10217-7
TUBI SENZA SALDATURA
ASTM / ASME:A/SA790
EN:10216-5
RACCORDI
ASTM / ASME:A/SA 815
EN:10253-4
VdTÜV
418
Reference:A/SA 240
Tensile Strength min N/mm2:620
Yield Point min N/mm2:450
Elongation 2” min %:25
Hardness max HB:293
Hardness max HRB:31
C% max:0.03
Mn% max:2.00
Si% max:1.00
P% max:0.03
S% max:0.02
Cr%:21 – 23
Ni%:4.5 – 6.5
Mo%:2.5 – 3.5
Fe%:Resto Balance
Cu% max:-
Other elements:N 0.08 – 0.2
Reference:A/SA 240
Tensile Strength min N/mm2:655
Yield Point min N/mm2:450
Elongation 2” min %:25
Hardness max HB:293
Hardness max HRB:31
C% max:0.03
Mn% max:2.00
Si% max:1.00
P% max:0.03
S% max:0.02
Cr%:22 – 23
Ni%:4.5 – 6.5
Mo%:3 – 3.5
Fe%:Resto Balance
Cu% max:-
Other elements:N 0.14 – 0.2
* Il grado più diffuso nella famiglia dei duplex, con PREN ? 35 (Nota a).
Si tratta di un acciaio inossidabile austenitico- ferritico legato con azoto, con stabilità della struttura migliorata e proprietà di resistenza elevata alla corrosione generale, localizzata e da stress meccanici.
Rende molto di più del grado 316L in quasi tutti i fluidi corrosivi.
Temperature di funzionamento tipiche sono -50/+280 °C (-60/540 °F).
Usi a temperature più basse potrebbero essere considerate, ma richiedono ulteriori precauzioni per le strutture saldate.
* Apparecchiature di controllo dell’inquinamento, industria chimica (reattori… ), produzione di Urea, torri di distillazione di acido acetico, impianti di acido fosforico (reattori), processi di acido solforico (idrometallurgia), pasta di legno e della carta, ambienti marini, acqua salmastra, operazioni di candeggio, impianti di acqua a circuito chiuso, applicazioni di trasformazione dei prodotti alimentari, del petrolio e del gas, comprese le applicazioni di gas acido.